FeCrAl Alloy Strip 0Cr21Al6 | 0.7mm Thick X 296mm Wide for Braking Resistor Applications
|
Détails sur le produit:
Conditions de paiement et expédition:
|
Description de produit détaillée
| Composition chimique: | 21%Cr 6%Al solde Fe | Dimensions: | 0,02-10 mm |
|---|---|---|---|
| Matériel: | Alliage | Forme: | fil |
| Application: | Appareils électroménagers | Résistivité (μΩ.m): | 1.42 |
| Résistance à la traction (≥ MPa): | 720 | Allongement (≥ %): | 20 |
| Limite conventionnelle d'élasticité (MPA de ≥): | 520 | Densité (g / cm3): | 7.16 |
| Température de fonctionnement (℃): | 1250 | OEM: | Disponible |
| Traitement de recuit: | recuit à l'hydrogène | Traitement de surface: | oxydation brillante |
| Certificat: | Pour les appareils électroniques |
FeCrAl Alloy Strip 0Cr21Al6 | 0.7mm Thick X 296mm Wide for Braking Resistor Applications
(Common Name:0Cr21Al6)
OhmAlloy142A is a iron-chromium-aluminium alloy (FeCrAl alloy) characterized by high resistance, low coefficient of electric resistance, high operating temperature, good corrosion resistance under high temperature.It is suitable for use at temperatures up to 1250°C.
Typical applications for OhmAlloy142A are used in electric ceramic cooktop,industrial furnace,heaters and catalytic purifier.
Normal composition%
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other |
| Max | |||||||||
| 0.06 | 0.025 | 0.025 | 0.70 | Max 1.0 | 19.0~22.0 | Max 0.60 | 5.0~7.0 | Bal. | - |
Typical Mechanical properties(1.0mm)
| Yield strength | Tensile Strength | Elongation |
| Mpa | Mpa | % |
| 520 | 720 | 20 |
Typical Physical properties
| Density (g/cm3) | 7.16 |
| Electrical resistivity at 20℃(Ωmm2/m) | 1.42 |
| Conductivity coefficient at 20℃ (WmK) | 13 |
| Coefficient of thermal expansion | |
| Temperature | Coefficient of Thermal Expansion x10-6/℃ |
| 20 ℃- 1000℃ | 14.7 |
| Specific heat capacity | |
| Temperature | 20℃ |
| J/gK | 13 |
| Melting point (℃) | 1500 |
| Max continuous operating temperature in air (℃) | 1250 |
| Magnetic properties | non-magnetic |
Temperature Factor of Electrical Resistivity
| 20℃ | 100℃ | 200℃ | 300℃ | 400℃ | 500℃ | 600℃ | 800℃ | 900℃ | 1000℃ | 1100℃ | 1200℃ | 1300℃ |
| 1 | 1.000 | 1.002 | 1.006 | 1.011 | 1.020 | 1.037 | 1.046 | 1.049 | 1.052 | 1.055 | 1.058 | - |
Style of supply
| Alloys Name | Type | Dimension | ||
| OhmAlloy142AW | Wire | D=0.03mm~8mm | ||
| OhmAlloy142AR | Ribbon | W=0.4~40 | T=0.03~2.9mm | |
| OhmAlloy142AS | Strip | W=8~250mm | T=0.1~3.0 | |
| OhmAlloy142AF | Foil | W=6~120mm | T=0.003~0.1 | |
| OhmAlloy142AB | Bar | Dia=8~100mm | L=50~1000 | |
Coordonnées
Ohmalloy Material Co.,Ltd
Personne à contacter: Mr. Qiu
Téléphone: +8613795230939
Envoyez votre demande directement à nous
Plus Alliage de Fecral
-
Alliage FeCr 23Al5
-
0Cr21Al6Nb Fil chauffant à résistance
-
Le fil résistant à la chaleur SUS314 de dureté élevée a laminé à froid la bande de l'acier inoxydable 314
-
GTS résistant à la chaleur 26 du fil 0cr25al5 28 30 pour les dessiccateurs infrarouges industriels
-
Encaissez l'alliage 0Cr25Al5 0.3mm x 60mm, bande électrique de chauffage, noyau de chauffage, élément de FeCrAl de résistance de tube de raidum
-
FeCrAl alliage plat fil de chauffage Cr23Al5 (Alchrome DK) 1400°C Max résistant à l'oxydation ASTM B603